The visual effect achieved from the final headlamp reflector is of the utmost importance and a quality powder primer is the key. The powder coating covers defects in the fabricated part and provides a smooth, corrosion resistant and high reflection finish for the vacuum metallization process. MT-A1270 is an epoxy coating for the application to headlamp reflector casing to provide corrosion protection with a high degree of smoothness in a thin film, prior to the process of metallization under vacuum.
Свойства порошка
| Химический тип | эпоксидная смола |
| Area of usage | Automotive headlamp reflectors |
| Particle Size Distributon | D50 = 26 – 32 µm Sympatec laser D50 = 30 – 36 µm Malvern laser |
| Внешний вид | Extremely smooth, high gloss |
| Цвет | Clear-brown |
| Блеск (60°) | 100 – 120 ГУ |
| Плотность (г / см3) | 1.10 ± 0.10 |
| Gel time at 200°C | 80 - 95 сек. |
| Условия после отверждения | 240°C object temperature, 30 minutes holding time (Variations due to oven conditions can be possible but it must be assured by the applicator that it works in his system) |
| Заполнитель | электростатический |
| Стабильность хранения | under dry, cool (<23°C) conditions, at least 6 months from production date |
Условия испытаний
The results are based on mechanical and chemical tests which (unless otherwise indicated) have been carried out under laboratory conditions and are given for guidance only. Actual product performance will depend upon the circumstances under which the product is used.
| Запечатываемый материал | Стальные панели |
| предварительная обработка | Bonder (WH/60/OC) iron phosphate |
| Толщина пленки | 40 - 60 мкм |
| График лечения | 30 minutes 240°C, post cure |
Механические испытания
| прилипание | ISO 2409 | Gt 0 |
| Твердость | ISO 2818 | ≥ 125 |
Предварительная обработка
Steel surfaces to be coated must be clean and free from grease. For maximum protection it is essential to pre-treat components prior to the application of MT-A1270. Iron Phosphate and Zinc Phosphate of ferrous metals improve corrosion resistance.
Заполнитель
MT-A1270 powders can be applied by manual or automatic electrostatic spray equipment. It is recommended that for consistent application and appearance product be fluidized during application.