MT-310 is a series of polyester resin based thermo-setting powder coatings, without TGIC with specific antimicrobial activity. The MT-310 resin system is warning label free. The pigments used in the MT-310 series restrict the field of application of this powder coatings class to interior uses. MT-310 AM is a high-quality powder coating designed to meet decorative and functional demands. Additionally, MT-310 AM uses antimicrobial technology to reduce the number of microbes such as bacteria and mold. Test results have proven a reduction of bacteria and mold up to 99.9%.
Свойства порошка
| Типичное значение | |
| Химический тип | Polyester – TGIC Free |
| Плотность | 1.2 – 1.9 г/см³, в зависимости от цвета и эффекта |
| Рекомендуемая толщина пленки | 60 - 90μm |
| Срок годности | 12 месяцев при температуре ниже 30 ºC |
| Условия хранения | В сухих, прохладных (≤ 30°C) условиях (открытые коробки необходимо плотно закрыть) |
| График отверждения | 8-16 мин при 200°С 10-20 мин при 180°С 20-40 мин при 170°С (при температуре объекта) |
Предварительная обработка
Aluminium components should receive a full multi-stage chromate conversion coating or suitable chrome-free pre-treatment or suitable pre-anodising to clean and condition the substrate. Detailed advice should be sought from the pre-treatment supplier. Iron phosphate and particularly Zinc phosphating of ferrous metals improves corrosion resistance. Aluminium substrates may require a chromate conversion coating.
Заполнитель
Powders can be applied by manual or automatic electrostatic spray equipment. A good protection is linked with the recommended film thickness. All powders can show small color differences from batch to batch, this is normal and unavoidable. Bonded products have better application properties than blended products (more stable) but attention should still be paid to line settings in order to avoid “marble effect”and changes in aspect after recycling. Products with different codes should not be mixed even if same colour and gloss.
Условия испытаний
Actual product performance will depend upon the circumstances under which the product is used. Testing has been determined under laboratory conditions using the following application properties and is for guidance only.
| Предварительная обработка | Фосфат цинка |
| Запечатываемый материал | Полированная сталь |
| График отверждения | 12 min at 200°C (object temperature) |
| Толщина пленки | 60 - 70μm |
Механические испытания
| Типичное значение | Метод/стандарт | |
| прилипание | Класс 0 | ISO 2409 (штриховка 2 мм) |
| Банки Эриксена | Проход 5 мм | стандартами качества ISO 1520 |
| Гибкость | Проход 5 мм | стандартами качества ISO 1519 |
| Твердость | Пройдено – проникновение в подложку отсутствует | ISO 1518-1 (2000g) |
| Ударопрочность | ≥30 kg.cm | ISO 6272-2 (d/r) |