Описание товара:
MT-PZ is a powder coating primer containing zinc which is designed to give enhanced corrosion protection of blasted mild steel. This duplex system combines cathodic protection and barrier effect. Dedicated to steel protection with a surface pre-treatment obtained by grit/shot, MT-PZ is based on a specific epoxy zinc rich formulation that promotes conductivity to enhance its cathodic protection. MT-PZ includes a specific anticorrosive function which improves protection even in cases of scratching.
Свойства порошка
| Химический тип | Термореактивная эпоксидная смола |
| Внешний вид | Гладкая |
| Цвет | серый |
| Рекомендуемая толщина пленки (мкм) | 70 - 120 мкм |
| Плотность (г / см3) | 2.9 ± 0.03 г/см³ |
| Заполнитель | электростатический |
| Память | В сухих, прохладных (≤ 30°C) условиях |
| Срок годности | Не менее 12 месяцев с даты производства |
предварительная обработка
Surface preparation depends upon the metal, the type of surface, its conditions and the required performance. See our recommendation for pretreatment to be used with MT-PZ.
| Запечатываемый материал | Механическая предварительная обработка | Химическая предварительная обработка |
| мягкая сталь | Дробеструйная обработка Sa 2.5 в соответствии с ISO NF EN 8501-1. Шероховатость: Rz 35 60 мкм / Ra 6-12 мкм. | запрещенный |
| Литая сталь | ||
| Электроцинковая сталь | запрещенный | |
| Сталь горячего цинкования | ||
| Zinc sprayed (gas flame/electrical deposition) |
Заполнитель
MT-PZ is suitable for corona electrostatic spraying. Tribo application is not recommended.
| Настройки приложения | Fluidizing air pressure: 1.5kg/cm2 initially then 1kg/cm2 Transport air pressure: 0.5 to 0.8 kg/cm Recommended voltage: 65 to 70kV |
| Curing limits | Primer should be cured, or at least gelled, using the recommended curing schedules, before application of the topcoat. The object temperature must not be below 110°C or above 180°C. The primer should be cured in a convection oven, optionally with infra-red heaters, with air temperature not exceeding 180°C. |
| Рекомендуемая толщина пленки | 70-120 мкм Хорошая защита связана с рекомендуемой толщиной пленки. |
| Утилизация | Trials, with suitable recycling equipment, must be carried out before commencing production. Attention should be paid to the ratio of new powder, a minimum of 70% must be used. Gun nozzles must be cleaned every 30 minutes. |