MT-PZ is a powder coating primer containing zinc which is designed to give enhanced corrosion protection of mild steel. This duplex system combines cathodic protection and barrier effect. Dedicated to steel protection with a surface pre-treatment obtained by grit/shot. MT- PZ is based on a specific epoxy zinc rich formulation that brings conductivity to enable the cathodic protection. MT-PZ includes a specific anticorrosive function which improves the protection in case of scratch.
Свойства порошка
| Химический тип | Термореактивная эпоксидная смола |
| Внешний вид | Гладкая |
| Цвет | серый |
| Рекомендуемая толщина пленки (мкм) | 70 - 120 мкм |
| Плотность (г / см3) | 2.9 ± 0.03 г/см³ |
| Заполнитель | электростатический |
| Память | В сухих, прохладных (≤ 30°C) условиях |
| Срок годности | Не менее 12 месяцев с даты производства |
предварительная обработка
Surface preparation depends upon the metal, the type of surface, its conditions and the required performance. See our recommendation for pretreatment to be used with MT- PZ.
| Запечатываемый материал | Механическая предварительная обработка | Химическая предварительная обработка |
| мягкая сталь | Дробеструйная обработка Sa 2.5 в соответствии с ISO NF EN 8501-1. Шероховатость: Rz 35 60 мкм / Ra 6-12 мкм. | запрещенный |
| Литая сталь | ||
| Электроцинковая сталь | запрещенный | |
| Сталь горячего цинкования | ||
| Zinc sprayed (gas flame/electrical deposition) |
Заполнитель
MT-PZ is suitable for corona electrostatic spraying. Tribo application is not recommended.
| Настройки приложения | Fluidizing air pressure: 1.5kg/cm² initially then 1kg/cm² Transport air pressure: 0.5 to 0.8 kg/cm Recommended voltage: 65 to 70kV |
| Curing limits | Primer should be cured, or at least gelled, using the recommended curing schedules, before application of the topcoat. The object temperature must not be below 110°C or above 180°C. The primer should be cured in a convection oven, optionally with infra-red heaters, with air temperature not exceeding 180°C. |
| Рекомендуемая толщина пленки | 70-120 мкм Хорошая защита связана с рекомендуемой толщиной пленки. |
| Утилизация | Trials, with suitable recycling equipment, must be carried out before commencing production. Attention should be paid to the ratio of new powder, a minimum of 70% must be used. Gun nozzles must be cleaned every 30 minutes. |